Using a 3-step, water-based spray application process, the ChromeFX™ spray system will place a highly durable coating of real metal on almost any substrate without using any toxic metals. This coating duplicates the look and feel of real chrome and can be further customized to replicate precious metals such as gold, silver, brass, etc..
Please see the Technical Data Sheets for detailed information on each step of the application process.
|
| Performance Testing |
- Salt Spray Per ASTM B-117
- Results: Over 1050 hrs. with no evidence of corrosion.
- Wet tape adhesion per FED. Test method 141c, method 6301.2
- Specular Gloss/60 @ 395
- Impact adhesion 140 IN./LBS.
- Results: no failure past point of impact, passed test.
|
| Properties of Coated Surface |
| Technical Property |
Performance |
| Gloss @ 60º Angle |
5º to 80º |
| Impact Resistance |
Excellent |
| Adhesion |
Excellent |
| Humidity Resistance |
Excellent |
| Salt Spray Resistance |
Excellent |
| Chemical Resistance |
Very Good |
| Abrasion Resistance |
Excellent |
| Temperature and Humidity Cycling |
Pass |
| Mar Resistance |
Very Good |
| Distinctness of image (doi) |
Up to mirror like |
|
| Application Data Summary |
Layer |
Application |
Dry Film Thickness |
Air dry at 25°C (77°F) |
Force Dry (Plastics)
|
Pot life |
Basecoat |
Standard Spray |
0.8 to 1.0 mils |
48 hours |
8-10 hours at 50°C (130°F) |
4 hours |
ChromeFX |
Special Kit/Process |
0.1 mils |
1 hour |
10 minutes at 50°C (130°F) |
NA |
Topcoat |
Standard Spray |
0.8 to 1.0 mils |
12 hours |
1 hour at 50°C (130°F) |
4 hours |
|
———————————————————————————————————————
|
|
|
|
| |
How to Apply Chrome FX:
|
———————————————————————————————————————
|
|